Annealed 410 Stainless Steel Strip

Annealed 410 Stainless Steel Strip is the general purpose and most widely used of all the Martensitic grades of stainless steels. In its annealed condition it may be drawn, formed or shaped and because it is an air or oil quench hardening grade it can be hardened to high strength levels by subsequent heat treatments. AISI410 offers very good resistance to scaling up to 1200° F., and its mechanical properties are excellent, it is NOT recommended for applications in which severe corrosion is encountered. Type 410 is used for springs, scrapers, fasteners, hardware brackets, furnace parts and burners. It is magnetic in all conditions. Tensile strength (as annealed) min. 448MPA, yield strength minimum 206MPA, and elongation in 2 inches at 20%. For solution annealing, slow controlled cooling from 815/870° C. For hardening, heat to 925/1010°C. Quench in air or oil.

Available in 410 stainless strips, sheets, or cut lengths, in all thicknesses 0.01mm and thicker are obtainable and may be customized for you.

Mechanical Properties

Grade	Tensile Strength ksi (MPa) Min	Yield Strength 0.2% offset ksi (MPa) Min	Elongation (% in 50mm) Min	Hardness (Brinell) Max	Hardness (Rockwell B) Max
410	65 (450)	30 (205)	20	217	96

Equivalent Grades of 410 Stainless Steel Strip

STANDARD	UNS	JIS	WERKSTOFF NR.	AFNOR	BS	GOST	EN
410	S41000	SUS 410	1.4006	–	–	–	–

Applications
Requiring moderate corrrosion resisitance and high mechanical properties are indeal for stainless steel 410 strip,like Cutlery,Steam and gas turbine blades,Kitchen utensils,Dental and surgical instruments